产品展示-涂层背板

涂覆型光伏背板-双面含氟SCH300系列
SCH300系列背板三层(FEVE/PET/FEVE)结构具有优良的绝缘性、抗老化性和阻水性。外层三氟醚类FEVE氟涂层具有优异的抗环境腐蚀性能、自洁性和抗划伤性能,中间PET层具有良好的绝缘性能和阻水性能,内层FEVE涂层有非常好的抗紫外性能和良好的粘接性能。

SCH300 double fluorocarbon coating backsheet
SCH300 is double fluorocarbon coatings three layers sandwich structure, the outside and inside both are high weathering fluorocarbon coatings, and medium is high performance PET layer. It suits for long life protection of large PV power station.

项目Property 单位Unit 检测方法Test method SCH300系列(白色/黑色)
结构Structure     FEVE/PET/FEVE
A面含氟层厚度Side A thickness μm GB/T 6672-2001 25
PET厚度Thickness μm GB/T 6672-2001 250-300
B面含氟层厚度 Side B thickness μm GB/T 6672-2001 25
产品总厚度 Total thickness μm GB/T 6672-2001 300-350
拉伸强度(TD) Tensile strength N/10mm ASTM D882-2002 ≥120
拉伸强度(MD) Tensile strength N/10mm ASTM D882-2002 ≥120
拉伸率(TD) Elongation % ASTM D882-2002 ≥100
拉伸率(MD) Elongation % ASTM D882-2002 ≥90
热收缩率(TD) Shrinkage % ASTM D1204-2002 ≤1.0
热收缩率(MD) Shrinkage % ASTM D1204-2002 ≤0.6
层间附着力(FEVE/PET) Coat adhesion GB/T9286-1988 0
涂层与EVA剥离强度(初始) Peel strength N/10mm GB/T2790-1995 ≥40
涂层与EVA剥离强度(85℃/85% 1000小时) Peel strength N/10mm GB/T2790-1995 ≥40
水蒸气透过率 Water vapor transmittance g/m2·day ASTM F1249-2006 ≤2.5
局部放电电压 Partial discharge VDC IEC60664-1-2007 ≥1000
击穿电压强度 Breakdown voltage KV ASTM D149-1997 ≥18
色差变化(85℃/85% 2000小时) Color change ⊿E GB/T 11186.3-1989 ≤2.0
色差变化(UVB 4000小时) Color change ⊿E GB/T 11186.3-1989 ≤2.0